Mineral fiber compositions

ABSTRACT

Mineral fiber compositions are disclosed which, in a first embodiment, include the following components, indicated in weight percents: about 54 to about 70 percent SiO 2 , about 0 to about 4 percent Al 2  O 3 , about 0 to about 6 percent Na 2  O, about 0 to about 6 percent K 2  O, about 0 to about 6 percent MgO, about 10 to about 28 percent CaO, about 6 to about 17 percent total iron as FeO, and about 0 to about 5 percent TiO 2 , wherein the total weight percent of SiO 2  and Al 2  O 3  ranges from about 56 percent to about 72 percent, the total weight percent of MgO and CaO ranges from about 12 percent to about 28 percent, the total weight percent of Na 2  O and K 2  O does not exceed 6 percent, and the total weight percent of all components, including trace elements, if any, is 100 percent. In a second embodiment, the compositions include the following components, indicated in weight percents: about 50 to about 68 percent SiO 2 , about 0 to about 4 percent Al 2  O 3 , about 0 to about 6 percent K 2  O, about 0 to about 6 percent Na 2  O, about 0 to about 10 percent MgO, about 10 to about 28 percent CaO, about 6 to about 16 percent total iron as FeO, about 0 to about 5 percent TiO 2 , and about 0.5 to about 12 percent ZrO 2 , wherein the total weight of Na 2  O and K 2  O does not exceed 6 percent and the total weight of all components, including trace elements, if any, is 100 percent.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of U.S. patent application No. 08/741,849, filed Oct. 31, 1996 now abandoned.

TECHNICAL FIELD

This invention relates to mineral fiber compositions and, more particularly, to insulation products formed from fibers made from such compositions.

BACKGROUND OF THE INVENTION

Mineral fiber insulation is well known and has been a commercial product for an extended period of time. Such insulation typically is made from a nonwoven network of intertwined fibers that have been fiberized from a melt, by one of several processes discussed below, and that are held together by a binder. The binder may be any suitable material but quite commonly is a phenol-formaldehyde resin or a ureaformaldehyde resin. A conveyor typically collects the binder-coated fibers in the form of a blanket and the blanket is heat cured to produce the final insulation product. Insulation materials of various densities can be produced by varying the conveyor speed and the thickness of the cured insulation.

Glass wools are generally prepared by a rotary process, whereby a glass melt is dropped into a "spinner" having a peripheral wall having a multitude of holes therein, through which the glass is forced by centrifugal force to form fibers, which process gives excellent fiber yields, i.e., low "shot" contents and excellent insulating properties. However, the glasses used to produce these fibers have low softening temperatures so that their use is generally limited to only moderately high service temperatures.

Mineral wools, on the other hand, have higher softening and use temperatures and thus can typically be used in higher temperature environments. However, these compositions generally have forming temperatures which are too high for rotary fiberizing. Mineral wools are usually formed by external centrifuge processes that produce a lower fiber yield and a higher shot content than the rotary process. An example of a mineral wool intended to be fiberized by an external centrifuge process is disclosed in WO 96/00196.

Previously in the art mineral wool compositions have been reported which allegedly can be formed into fiber by a rotary process. (See International Patent Application Publications WO 95/01941 and WO 93/02977, U.S. Pat. No. 5,554,324, and European Patent Application EP 583 792). However, these compositions all contain high amounts of Na₂ O, K₂ O, and B₂ O₃, which can negatively affect the high temperature performance of the fiber, or high amounts of Al₂ O₃, which can decrease the biosolubility of the fiber.

Although mineral fibers have not been linked to disease in humans, it has become desirable to increase the biosolubility of mineral fibers. One would expect that increasing the solubility of mineral fibers would further decrease the time the fibers remain in a lung, if they were to be inhaled, and thus that the dissolution rate of mineral fibers in a saline solution having a composition similar to that existing in a human lung would be a good indicator of the biosolubility of such fibers. This dissolution rate can be improved by altering the chemical composition of a fiber. Previously in the art, it was thought that these alterations could not be made without impairing other properties of the fibers necessary for commercial purposes.

Accordingly, it is an object of the present invention to provide an improved mineral fiber composition and an improved mineral fiber formed from such composition.

Another object of the present invention is to provide a mineral fiber useable in relatively high temperature environments.

A further object of the present invention is to provide a mineral fiber composition that may be formed into a mineral fiber in a rotary fiberizing process.

Yet another object of the present invention is to provide a mineral fiber that is relatively biosoluble, yet sufficiently durable.

More preferably, it is an object of the present invention to provide a mineral fiber composition that may be formed into a mineral fiber in a rotary fiberizing process, which fiber is usable in high temperature environments and is sufficiently durable.

More preferably, it is an object of the present invention to provide a mineral fiber composition that may be formed into a mineral fiber in a rotary fiberizing process, which fiber is usable in high temperature environments and is relatively biosoluble, yet sufficiently durable.

SUMMARY OF THE INVENTION

The above objects as well as other objects not specifically enumerated are accomplished by a mineral fiber composition according to a first embodiment of the present invention, which includes the following components, indicated in weight percents: about 54 to about 70 percent SiO₂, about 0 to about 4 percent Al₂ O₃, about 0 to about 6 percent Na₂ O, about 0 to about 6 percent K₂ O, about 0 to about 6 percent MgO, about 10 to about 28 percent CaO, about 6 to about 17 percent total iron as FeO, and about 0 to about 5 percent TiO₂, wherein the total weight percent of SiO₂ and Al₂ O₃ ranges from about 56 percent to about 72 percent, the total weight percent of MgO and CaO ranges from about 12 percent to about 28 percent, the total weight percent of Na₂ O and K₂ O does not exceed 6 percent, and the total weight percent of all components, including trace elements, if any, is 100 percent.

The above objects are also accomplished by a mineral fiber composition according to a second embodiment of the present invention, which includes the following components, indicated in weight percents: about 50 to about 68 percent SiO₂, about 0 to about 4 percent Al₂ O₃, about 0 to about 6 percent K₂ O, about 0 to about 6 percent Na₂ O, about 0 to about 10 percent MgO, about 10 to about 28 percent CaO, about 6 to about 16 percent total iron as FeO, about 0 to about 5 percent TiO₂, and about 0.5 to about 12 percent ZrO₂, wherein the total weight of Na₂ O and K₂ O does not exceed 6 percent and the total weight of all components, including trace elements, if any, is 100 percent.

The above objects are further accomplished by mineral wool insulation including mineral fibers having a composition according to the first embodiment of the present invention, and by a mineral wool insulation including mineral fibers having a composition according to the second embodiment of the present invention.

DETAILED DESCRIPTION AND PREFERRED EMBODIMENTS OF THE INVENTION

As will be discussed more fully below, mineral fiber compositions according to the present invention have relatively lower liquidus temperatures and relatively higher viscosities than a standard rockwool, thus allowing rotary fiberization thereof. For these compositions, the liquidus temperatures are generally less than about 2200° F. (1204° C.), and, more preferably, less than about 2180° F. (1193° C.). These relatively lower liquidus temperatures are due at least in part to the relatively low MgO content of the mineral fiber compositions. The viscosity of the compositions generally falls between about 150 and about 1000 poise at 2250° F. (1232° C.) and, more preferably, between about 200 and 800 poise at 2250° F. (1232° C.). With these properties, the compositions of this invention have sufficiently low liquidus temperatures and adequate viscosity ranges to allow these compositions to be used in a typical rotary fiberizing apparatus.

The compositions of the present invention are preferably resistant to high temperature degradation, such that they form wool products that can be used in relatively high temperature environments. The compositions of the present invention also preferably produce fibers which are relatively biosoluble, yet sufficiently durable to maintain a wool product's physical integrity over many years in the location at which it is installed. Such fibers preferably should not only be fairly inert to moisture attack at the installation site, but also capable of dissolving in a physiological medium, such as human lung fluid.

Like a standard rockwool composition described below, the compositions of the present invention have a relatively low Na₂ O+K₂ O content to help give the rotary fiberized product relative good high temperature resistance. However, the compositions of the present invention include, relative to a standard rockwool, moderately increased amounts of SiO₂, greatly reduced amounts of Al₂ O₃, and an increased Fe₂ O₃ content. In one embodiment of the invention, the compositions can also include an increased ZrO₂ content. As discussed more fully below, these changes can be implemented in varying degrees to produce compositions that are not only fiberizable by rotary methods, but also, in varying degrees, are resistant to high temperatures, durable, and preferably, relatively biosoluble.

A mineral fiber composition according to a first embodiment of the present invention include the following components, in about the indicated weight percents (as is standard practice in the art, the components are reported as oxides, even though essentially no such individual crystals are present):

    ______________________________________     Component       Weight Percent     ______________________________________     SiO.sub.2       54-70     Al.sub.2 O.sub.3                     0-4     Na.sub.2 O      0-6     K.sub.2 O       0-6     MgO             0-6     CaO             10-28     Total Iron as FeO*                      6-17     TiO.sub.2       0-5     SiO.sub.2 + Al.sub.2 O.sub.3                     56-72     Na.sub.2 O + K.sub.2 O                     0-6     MgO + CaO       12-28     ______________________________________

* Iron is present as both Fe²⁺ and Fe³⁺ or in oxide form as FeO and Fe₂ O₃. Since the fraction of Fe²⁺ and Fe³⁺ is unknown, the total of both iron oxides is expressed herein as FeO.

Preferred ranges for components of the composition according to the first embodiment of the invention are as follows, in about the indicated weight percents:

    ______________________________________     Component       Weight Percent     ______________________________________     SiO.sub.2       56-68     Al.sub.2 O.sub.3                     0-3     Na.sub.2 O      0-5     K.sub.2 O       0-5     MgO             1-6     CaO             10-25     Total Iron as FeO                      8-16     TiO.sub.2       0-4     SiO.sub.2 + Al.sub.2 O.sub.3                     58-71     K.sub.2 O + Na.sub.2 O                     0-5     MgO + CaO       14-26     ______________________________________

More preferred ranges for components of the composition according to the first embodiment of the invention are as follows, in about the indicated weight percents:

    ______________________________________     Component       Weight Percent     ______________________________________     SiO.sub.2       58-65     Al.sub.2 O.sub.3                     0-3     Na.sub.2 O      0-4     K.sub.2 O       0-4     MgO             2-5     CaO             11-20     Total Iron as FeO                      9-13     TiO.sub.2       0-3     SiO.sub.2 + Al.sub.2 O.sub.3                     60-68     Na.sub.2 O + K.sub.2 O                     0-4     MgO + CaO       17-22     ______________________________________

Comparative Example 1

The table below shows the approximate weight percent composition and some properties of a commercial rockwool, i.e., Composition A, as well as the same for seven mineral wool compositions, i.e., Compositions B through H, according to the first embodiment of the present invention.

    ______________________________________     Component              A      B      C    D    E    F    G    H     ______________________________________     SiO.sub.2              45.4   62.00  63.0 62.0 62.0 64.0 63.0 62.0     Al.sub.2 O.sub.3              13.7   3.00   2.0  3.0  3.9  1.0  2.0  3.0     Na.sub.2 O              2.2    2.60   2.5  2.5  5.5  2.5  2.5  2.5     K.sub.2 O              0.5    0.90   0.5  0.5  0.5  0.5  0.5  0.5     MgO      11.3   4.50   3.5  2.5  3.0  2.5  2.5  3.52     CaO      19.6   13.35  18.5 19.5 16.0 19.5 19.5 18.48     TiO.sub.2              1.4    1.90   0.2  0.2  0.2  0.2  0.2  0.2     Total Iron As              5.4    11.75  9.8  9.8  9.8  9.8  9.8  9.8     FeO     Liquidus(°F.)              2251   2171   2160 2158 2101 --   2196 2180     Liquidus(°C.)              1231   1188   1182 1181 1149 --   1202 1193     Viscosity.sup.1              104    442    328  344  --   --   --     % Shrink.sup.2              6      3      --   4    --   11   4     Dissol. Rate.sup.3              15     42     --   42   --   107  94     ______________________________________      .sup.1 Measured in poise at 2250° F. (1230° C.).      .sup.2 Measured at 930° C.      .sup.3 Measured as ng/cm.sup.2hr in a model physiological saline solution      at 37° C. with a flow rate of 0.2 mL per minute

A standard rockwool's lack of suitability for fiberizing by a rotary process is evidenced from the values given for Composition A. Specifically, Composition A has a liquidus temperature of 2251° F. (1231° C.), which is generally too high to achieve economical results from the typical rotary process now used. Also, Composition A has a viscosity of 104 poise at 2250° F. (1230° C.), which is generally too low to achieve good quality fibers with low shot content. In addition, the dissolution rate of Composition A, 15 ng/cm² -hr, is much lower than desired.

In contrast, Composition B has a liquidus temperature of 2171° F. (1188° C.) and a viscosity of 442 poise at 2250° C., Composition C has a liquidus temperature of 2160° F. (1182° C.) and a viscosity of 328 poise, and Composition D has a liquidus temperature of 2158° F. (1181° C.) and a viscosity of 344 poise, which indicates that Compositions B, C and D should be economically fiberizable, with fairly good fiber quality, using relatively standard rotary fiberization methods. In addition, the high temperature resistances of Compositions B and D compare well with that of Composition A, i.e., 3 and 4 percent linear shrink, respectively, vs. 6 percent linear shrink at 930° C. The percent linear shrink is a measure of fire resistance determined from a standard fire test, with less shrinkage indicating better fire performance. Further, Compositions B and D each has an improved dissolution rate of 42 ng/cm² -hr with respect to Composition A.

It is believed that the temperature resistances of compositions according to the first embodiment of the invention are due to the relatively low alkali, i.e., Na₂ O+K₂ O, contents thereof, and that the relatively low liquidus temperatures thereof are due at least in part to their relatively low MgO contents. In addition, it is believed that the relatively improved dissolution rates of the compositions are due to the low alumina levels thereof. As can be seen from Compositions F and G, these improved dissolution rates can be quite high, i.e., 107 ng/cm² -hr for Composition F, although potentially at some sacrifice of other properties for certain compositions, i.e., the higher liquidus temperature of Composition G. Accordingly, alternative compositions according to a second embodiment of the present invention are desirable in some instances to produce certain combinations of liquidus, viscosity and dissolution rate, while retaining temperature resistance.

Mineral fiber compositions according to a second embodiment of the invention include the following components, in about the indicated weight percents:

    ______________________________________                     WEIGHT     COMPONENT       PERCENT     ______________________________________     SiO.sub.2       50-68     Al.sub.2 O.sub.3                     0-4     K.sub.2 O       0-6     Na.sub.2 O      0-6     MgO              0-10     CaO             10-28     Total Iron as FeO                      6-16     TiO.sub.2       0-5     ZrO.sub.2       0.5-12     Na.sub.2 O + K.sub.2 O                     0-6     ______________________________________

Preferred ranges for components of the composition according to the second embodiment of the invention are as follows, in about the indicated weight percents:

    ______________________________________                     WEIGHT     COMPONENT       PERCENT     ______________________________________     SiO.sub.2       52-66     Al.sub.2 O.sub.3                       0-3.5     K.sub.2 O       0-5     Na.sub.2 O      0-5     MgO             1-8     CaO             11-25     Total Iron as FeO                      7-15     TiO.sub.2       0-4     ZrO.sub.2        1-11     Na.sub.2 O + K.sub.2 O                     0-5     ______________________________________

More preferred ranges for components of the composition according to the second embodiment are as follows, in about the indicated weight percents:

    ______________________________________     COMPONENT       WEIGHT PERCENT     ______________________________________     SiO.sub.2       54-64     Al.sub.2 O.sub.3                       0-3.5     K.sub.2 O         0-4.5     Na.sub.2 O        0-4.5     MgO             1-4     CaO             12-23     Total Iron as FeO                      7-14     TiO.sub.2       0-3     ZrO.sub.2       1-9     Na.sub.2 O + K.sub.2 O                       0-4.5     ______________________________________

More preferred ranges for components of the compositions according to the second embodiment of the invention are as follows, in about the indicated weight percents:

    ______________________________________     COMPONENT       WEIGHT PERCENT     ______________________________________     SiO.sub.2       57-62     Al.sub.2 O.sub.3                     0.5-2     K.sub.2 O       0-4     Na.sub.2 O      0-3     MgO             2-4     CaO             16-22     Total Iron as FeO                      7-12     TiO.sub.2       0-2     ZrO.sub.2       1-5     Na.sub.2 O + K.sub.2 O                       0-4.5     ______________________________________

EXAMPLE 2

Specific examples of compositions according to the second embodiment of this invention are shown in the following table with quantities being presented by approximate weight percent of total composition.

    __________________________________________________________________________     COMPONENT            I  J  K  L  M  N  O  P  Q  R  S     __________________________________________________________________________     SiO.sub.2            60 60 60 56 60 62 62 60 60.5                                       60.06                                          60     Al.sub.2 O.sub.3            3  3  2  3  3  3  3  2  0.5                                       1.5                                          1.34     Na.sub.2 O            2.5               2.5                  0.25                     2.5                        2.5                           2.5                              2.5                                 025                                    4  2.5                                          2.5     K.sub.2 O            0.5               0.5                  2.75                     0.5                        0.5                           0.5                              0.5                                 2.75                                    0.16                                       0.38                                          0.35     MgO    2.57               2.4                  2.5                     2.17                        2.05                           3.2                              2.88                                 2  3.14                                       3.07                                          3.07     CaO    19.94               18.6                  19.5                     16.83                        15.95                           16.8                              15.12                                 18 19.86                                       19.43                                          19.43     BaO    0  0  0  0  3.0                           0  0  0  0  0  0     TiO.sub.2            0.2               0.2                  0.2                     0.2                        0.2                           0.2                              0.2                                 0.2                                    0.06                                       0.06                                          0.06     Total Iron As     FeO    9.8               9.8                  9.8                     9.8                        9.8                           9.8                              9.8                                 11.8                                    9.75                                       10 10     ZrO.sub.2            1.5               3  3  9  3  2  4  3  2.03                                       3  3.25     Liquidus (° F.)            2110               2137                  2135                     2151                        2091                           2121                              2137                                 2117                                    2180                                       2155                                          2150     Liquidus (° C.)            1154               1169                  1168                     1177                        1144                           1161                              1169                                 1158     Viscosity.sup.1               366                        254     % Shrink.sup.2            41.7               12.2                  5.5                  7.1                                          163     Dissol Rate.sup.3               44.3                 144                                       74 80     __________________________________________________________________________

As can be seen by comparing Composition D with Composition J, the compositions are very similar, with Composition J having 3 percent ZrO₂ substituted for 2 percent SiO₂ and 1 percent CaO in Composition D. As can further be seen, this addition of ZrO₂ in Composition J produces a moderate reduction in the liquidus temperature of that composition as compared to Composition D, and a moderate increase in viscosity at 2250° F. Both changes are desirable, to improve the economics and fiber quality of rotary fiberization, respectively. As can also be seen, Composition J has a dissolution rate which is comparable to that of Composition D, and a temperature resistance that is relatively good.

The percent linear shrink of Composition I was measured and was determined to be 41.7%. This is a high rate of linear shrinkage when compared with the linear shrinkages for Compositions D and J. The high rate of linear shrinkage of Composition I can be attributed to both its SiO₂ concentration and its ZrO₂ concentration. The formulation of Composition I includes 2% less SiO₂ and 1.5% more ZrO₂ than Composition D. Also, Composition I has the same percentage of SiO₂ but 1.5% less ZrO₂ than Composition J. The relatively high linear shrinkage for Composition I indicates that, for that particular composition, while maintaining the other components relatively constant, the addition of only 1.5% ZrO₂ does not sufficiently make up for the high temperature resistance which is lost when 2% of SiO₂ is removed from the composition. However, as can be seen from comparing Composition D with Composition J, the addition of 3% of ZrO₂ substituted for the 2% loss of SiO₂ does adequately make up for the high temperature resistance which is lost when the SiO₂ is removed.

The biosolubility of Composition J, while much improved relative to a standard rockwool such as Composition A, is still lower than achieved by a more preferred embodiment of the invention. An increase in such biosolubility as a result of a decrease in Al₂ O₃ content can be seen by comparing Composition J with Compositions R and S. Compositions R and S are similar to Composition J, with roughly 1.5 percent Al₂ O₃ replaced with roughly 1.5 percent CaO and MgO, collectively. Compositions R and S have dissolution rates in a model physiological saline solution, at 37° C. with a flow rate of 0.2 mL per minute, of 74 and 80 ng/cm² -hr, respectively, as compared with 42 and 44.3 ng/cm² -hr, respectively, for Compositions D and J. Compositions R and S also have relatively good high temperature resistance, and liquidus temperatures similar to that of Composition D. The viscosity of Composition S also is in a range that should allow for relatively good fiber quality in a rotary fiberizing process (the viscosity of Composition R has not been tested, but is expected to also be within an acceptable range). For these reasons, Compositions R and S are at this time the most preferred embodiments of the present invention.

As stated above, the compositions of this invention can be formed into mineral wool fibers by a rotary fiberizing apparatus. If used to create an insulation product, the fibers can be coated with a binder to hold the insulation product together. The fibers can also be coated with lubricating agents, wetting agents, antistatic agents and extenders or stabilizers. Typically, the fibers are coated as they are attenuated from the fiberizing apparatus. However, one skilled in the art will appreciate that the fibers can be coated at any time in the insulation formation process. Once the fibers have been attenuated from the fiberizing apparatus, the fibers are typically collected on a porous conveyor belt or other collection apparatus to be formed into an insulation product.

Although the compositions of this invention have been described above as being primarily useful in mineral wool insulation products, one skilled in the art will understand that the compositions of this invention can be used to form mineral fibers useful in other applications than insulation. For example, fibers formed from the compositions of this invention can also be used to form air handling ducts, ceiling panels and acoustical panels.

While certain representative embodiments and details have been shown for purposes of illustrating the invention, it will be apparent to those of skill in the art that various changes and modifications can be made to the compositions of this invention without departing from the scope of the invention, which is defined in the appended claims. 

What is claimed is:
 1. A mineral fiber composition consisting essentially of the following components, indicated in weight percents:about 54 to about 70 percent SiO₂, about 0 to about 4 percent Al₂ O₃, about 0 to about 6 percent Na₂ O, about 0 to about 6 percent K₂ O, about 0 to about 6 percent MgO, about 10 to about 28 percent CaO, about 6 to about 17 percent total iron as FeO, and about 0 to about 5 percent TiO₂, wherein the total weight percent of SiO₂ and Al₂ O₃ ranges from about 56 percent to about 72 percent, the total weight percent of MgO and CaO ranges from about 12 percent to about 28 percent, the total weight percent of Na₂ O and K₂ O does not exceed 6 percent, the total weight percent of Al₂ O₃ and FeO is not less than 12.8 percent, and the total weight percent of all components, including trace elements, if any, is 100 percent.
 2. The mineral fiber composition according to claim 1, consisting essentially of the following components indicated in weight percents:about 56 to about 68 percent SiO₂, about 0 to about 3 percent Al₂ O₃, about 0 to about 5 percent Na₂ O, about 0 to about 5 percent K₂ O, about 1 to about 6 percent MgO, about 10 to about 25 percent CaO, about 8 to about 16 percent total iron as FeO, and about 0 to about 4 percent TiO₂, wherein the total weight percent of SiO₂ and Al₂ O₃ ranges from about 58 percent to about 71 percent, the total weight percent of MgO and CaO ranges from about 14 percent to about 26 percent, the total weight percent of Na₂ O and K₂ O does not exceed 5 percent, and the total weight percent of all components, including trace elements, if any, is 100 percent.
 3. The mineral fiber composition according to claim 1, consisting essentially of the following components indicated in weight percents:about 58 to about 65 percent SiO₂, about 0 to about 3 percent Al₂ O₃, about 0 to about 4 percent K₂ O, about 0 to about 4 percent Na₂ O, about 2 to about 5 percent MgO, about 11 to about 20 percent CaO, about 9 to about 13 percent total iron as FeO, and about 0 to about 3 percent TiO₂, wherein the total weight percent of SiO₂ and Al₂ O₃ ranges from about 60 percent to about 68 percent, the total weight percent of MgO and CaO ranges from about 17 percent to about 22 percent, the total weight percent of Na₂ O and K₂ O does not exceed 4 percent, and the total weight percent of all components, including trace elements, if any, is 100 percent.
 4. The mineral fiber composition according to claim 1, consisting essentially of the following components in the indicated weight percents:about 62 percent SiO₂, about 3 percent Al₂ O₃, about 2.6 percent K₂ O, about 0.9 percent Na₂ O, about 4.5 percent MgO, about 13.4 percent CaO, about 1.9 percent TiO₂, and about 11.7 percent total iron as FeO.
 5. The mineral fiber composition according to claim 1, consisting essentially of the following components in the indicated weight percents:about 62 percent SiO₂, about 3 percent Al₂ O₃, about 2.5 percent Na₂ O, about 0.5 percent K₂ O, about 2.5 percent MgO, about 19.5 percent CaO, about 0.2 percent TiO₂, and about 9.8 percent total iron as FeO.
 6. The mineral fiber composition according to claim 1, consisting essentially of the following components in the indicated weight percents:about 63 percent SiO₂, about 3 percent Al₂ O₃, about 5.5 percent Na₂ O, about 0.5 percent K₂ O, about 3 percent MgO, about 16 percent CaO, about 0.2 percent TiO₂, and about 9.8 percent total iron as FeO.
 7. The mineral fiber composition according to claim 1, consisting essentially of the following components in the indicated weight percents:about 64 percent SiO₂, about 1 percent Al₂ O₃, about 2.5 percent Na₂ O, about 0.5 percent K₂ O, about 2.5 percent MgO, about 19.5 percent CaO, about 0.2 percent TiO₂, and about 9.8 percent total iron as FeO.
 8. The mineral fiber composition of claim 1, consisting essentially of the following components in the indicated weight percents:about 63 percent SiO₂, about 2 percent Al₂ O₃, about 2.5 percent Na₂ O, about 0.5 percent K₂ O, about 2.5 percent MgO, about 19.5 percent CaO, about 0.2 percent TiO₂, and about 9.8 percent total iron as FeO.
 9. The mineral fiber composition according to claim 1, wherein the composition has a liquidus temperature below about 2200° F. (1204° C.) and a viscosity which ranges between about 100 and about 1000 poise at 2250° F. (1232° C.).
 10. Mineral wool insulation comprising mineral fibers having the composition of claim
 1. 11. A mineral fiber composition consisting essentially of the following components in the indicated weight percents:about 63 percent SiO₂, about 2 percent Al₂ O₃, about 2.5 percent Na₂ O, about 0.5 percent K₂ O, about 3.5 percent MgO, about 18.5 percent CaO, about 0.2 percent TiO₂, and about 9.8 percent total iron as FeO.
 12. A mineral fiber composition consisting essentially of the following components, indicated in weight percents:about 50 to about 68 percent SiO₂, about 0 to about 4 percent Al₂ O₃, about 0 to about 6 percent K₂ O, about 0 to about 6 percent Na₂ O, about 0 to about 10 percent MgO, about 10 to about 28 percent CaO, about 6 to about 16 percent total iron as FeO, about 0 to about 5 percent TiO₂, and about 0.5 to about 12 percent ZrO₂, wherein the total weight of Na₂ O and K₂ O does not exceed 6 percent and the total weight of all components, including trace elements, if any, is 100 percent.
 13. The mineral fiber composition according to claim 12, consisting essentially of the following components indicated in weight percents:about 52 to about 66 percent SiO₂, about 0 to about 3.5 percent Al₂ O₃, about 0 to about 5 percent K₂ O, about 0 to about 5 percent Na₂ O, about 1 to about 8 percent MgO, about 11 to about 25 percent CaO, about 7 to about 15 percent total iron as FeO, about 0 to about 4 percent TiO₂, and about 1 to about 11 percent ZrO₂, wherein the total weight of Na₂ O and K₂ O does not exceed 5 percent and the total weight of all components, including trace elements, if any, is 100 percent.
 14. The mineral fiber composition according to claim 12, consisting essentially of the following components indicated in weight percents:about 54 to about 64 percent SiO₂, about 0 to about 3.5 percent Al₂ O₃, about 0 to about 4.5 percent K₂ O, about 0 to about 4.5 percent Na₂ O, about 1 to about 4 per MgO, about 12 to about 23 percent CaO, about 7 to about 14 percent total iron as FeO, about 0 to about 3 percent TiO₂, and about 1 to about 9 percent ZrO₂, wherein the total weight of Na₂ O and K₂ O does not exceed 4.5 percent and the total weight of all components, including trace elements, if any, is 100 percent.
 15. The mineral fiber composition according to claim 12, consisting essentially of the following components indicated in weight percents:about 57 to about 62 percent SiO₂, about 0.5 to about 2.0 percent Al₂ O₃, about 0 to about 4 percent K₂ O, about 0 to about 3 percent Na₂ O, about 2 to about 4 percent MgO, about 16 to about 22 percent CaO, about 7 to about 12 percent total iron as FeO, about 0 to about 2 percent TiO₂, about 1 to about 5 percent ZrO₂, wherein the total weight of Na₂ O+K₂ O does not exceed 4.5 percent and the total weight of all components, including trace elements, if any, is 100 percent.
 16. The mineral fiber composition according to claim 12, consisting essentially of the following components indicated in weight percents:about 60 percent SiO₂, about 3 percent Al₂ O₃, about 2.5 percent Na₂ O, about 0.5 percent K₂ O, about 2.6 percent MgO, about 19.9 percent CaO, about 0.2 percent TiO₂, about 9.8 percent total iron as FeO and about 1.5 percent ZrO₂.
 17. The mineral fiber composition according to claim 12, consisting essentially of the following components indicated in weight percents:about 60 percent SiO₂, about 3 percent Al₂ O₃, about 2.5 percent Na₂ O, about 0.5 percent K₂ O, about 2.4 percent MgO, about 18.6 percent CaO, about 0.2 percent TiO₂, about 9.8 percent total iron as FeO and about 3 percent ZrO₂.
 18. The mineral fiber composition according to claim 12, consisting essentially of the following components indicated in weight percents:about 60 percent SiO₂, about 2 percent Al₂ O₃, about 0.25 percent Na₂ O, about 2.75 percent K₂ O, about 2.5 percent MgO, about 19.5 percent CaO, about 0.2 percent TiO₂, about 9.8 percent total iron as FeO and about 3 percent ZrO₂.
 19. The mineral fiber composition according to claim 12, consisting essentially of the following components indicated in weight percents:about 56 percent SiO₂, about 3 percent Al₂ O₃, about 2.5 percent Na₂ O, about 0.5 percent K₂ O, about 2.2 percent MgO, about 16.8 percent CaO, about 0.2 percent TiO₂, about 9.8 percent total iron as FeO and about 9 percent ZrO₂.
 20. The mineral fiber composition according to claim 12, consisting essentially of the following components, indicated in weight percents:about 60 percent SiO₂, about 3 percent Al₂ O₃, about 2.5 percent Na₂ O, about 0.5 percent K₂ O, about 2.1 percent MgO, about 16 percent CaO, about 0.2 percent TiO₂, about 9.8 percent total iron as FeO, and about 3 percent ZrO₂, and further including about 3 percent BaO.
 21. The mineral fiber composition according to claim 12, consisting essentially of the following components indicated in weight percents:about 62 percent SiO₂, about 3 percent Al₂ O₃, about 2.5 percent Na₂ O, about 0.5 percent K₂ O, about 3.2 percent MgO, about 16.8 percent CaO, about 0.2 percent TiO₂, about 9.8 percent total iron as FeO and about 2 percent ZrO₂.
 22. The mineral fiber composition according to claim 12, consisting essentially of the following components indicated in weight percents:about 62 percent SiO₂, about 3 percent Al₂ O₃, about 2.5 percent Na₂ O, about 0.5 percent K₂ O, about 2.9 percent MgO, about 15.1 percent CaO, about 0.2 percent TiO₂, about 9.8 percent total iron as FeO and about 4 percent ZrO₂.
 23. The mineral fiber composition according to claim 12, consisting essentially of the following components indicated in weight percents:about 60 percent SiO₂, about 2 percent Al₂ O₃, about 0.25 percent Na₂ O, about 2.75 percent K₂ O, about 2 percent MgO, about 18 percent CaO, about 0.2 percent TiO₂, about 11.8 percent total iron as FeO and about 3 percent ZrO₂.
 24. The mineral fiber composition according to claim 12, consisting essentially of the following components indicated in weight percents:about 60.5 percent SiO₂, about 0.5 percent Al₂ O₃, about 4 percent Na₂ O, about 0.2 percent K₂ O, about 3.1 percent MgO, about 19.9 percent CaO, about 0.06 percent TiO₂, about 9.75 percent total iron as FeO and about 2 percent ZrO₂.
 25. The mineral fiber composition according to claim 12, consisting essentially of the following components indicated in weight percents:about 60 percent SiO₂, about 1.5 percent Al₂ O₃, about 2.5 percent Na₂ O, about 0.4 percent K₂ O, about 3.1 percent MgO, about 19.4 percent CaO, about 0.06 percent TiO₂, about 10 percent total iron as FeO and about 3.0 percent ZrO₂.
 26. The mineral fiber composition according to claim 12, consisting essentially of the following components indicated in weight percents:about 60 percent SiO₂, about 1.3 percent Al₂ O₃, about 2.5 percent Na₂ O, about 0.4 percent K₂ O, about 3.1 percent MgO, about 19.4 percent CaO, about 0.06 percent TiO₂, about 10 percent total iron as FeO and about 3.3 percent ZrO₂.
 27. Mineral wool insulation comprising mineral fibers having the composition of claim
 12. 